The effect of silane modification on morphology and properties of ABS/SGF composites
محل انتشار: دوازدهمین کنگره ملی مهندسی شیمی ایران
سال انتشار: 1387
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,725
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
NICEC12_451
تاریخ نمایه سازی: 30 شهریور 1387
چکیده مقاله:
acrylonitrile-butadiene-styrene(ABS) / short glass fiber(SGF) composites were prepared. The effect of fiber volume fraction on the properties of composites was investigated, and test results were compared with theorical equations. SEM micrographs confirmed the
reports in other studies that the adhesion between ABS and neat glass fiber is poor. Silane coupling agents with different rganofunctional
groups were used to improve the interface. The role of these coupling agents was studied by comparing processability, mechanical and
physical properties of the composites containing different silane-treated glass fibers. It seems that using coupling agents specially those with more effective functional groups reduces the deviation of properties from theory. The affinity of different functional groups to ABS as well as the strength of chemical and physical bandings formed during the reaction of silane modification, decides the effectiveness of the relative coupling agent. By properties and morphology analysis we concluded that Tricholorovinyle Silane seems to be the best coupling agent between others, for this composite. This conclusion is supported by the theorical possibility.
کلیدواژه ها:
نویسندگان
Shirin Shokoohi
۱,۲Department of polymer engineering, Amirkabir University of Technology
Ahmad Aref Azar
Department of polymer engineering, Amirkabir University of Technology
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :