The effect of temperature and topological defects on H2 adsorption on carbon nanotubes

Physisorption of molecular hydrogen on pristine single-walled carbon nanotube and three types of topologically defected nanotubes (Stone-wales, vacancy and interstitial defects) at different temperatures 77, 300 and 600 K has been investigated via molecular dynamics simulation. The applied intermolecular forces are modeled using the modified form of the well-known Lennard-Jones potential based on the nanotube curvature. The adsorption/desorption cycle was followed by increasing the operating temperature under the pressure of 1 bar. The simulation results of exposing 6.5%wt of H2 on defected and pristine (3,3) nanotubes reveal that the highest and lowest adsorption energies and storage capacities are obtained from the nanotubes with interstitial and vacancy defects, respectively.

کلیدواژه ها:

Single-walled carbon nanotube ، Hydrogen storage ، topological defect ، molecular dynamics simulation