Synthesis of U3O8 with secondary honeycomb morphology
سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 566
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
PENPP01_145
تاریخ نمایه سازی: 19 خرداد 1396
چکیده مقاله:
Uranium enrichment engages UF6 gas, which is prepared from U3O8 powder. U3O8 powder has been prepared by some methods like: chemical transport reactions, solid –state thermal decomposition of a new dioxidouranium (VI) complex, surfactant templating-crystal growth technique. In this research, by constant current density of 5 mA.cm-2, we used galvanostatic electro-deposition to synthesize a sample of UO3 by a simple, fast, and clean method in a closed system. After deposition of UO2(OH)2 at electrode surface, the sample was scratched and oxidized by the thermal annealing at 300-700 °C to form U3O8. powder. The as-prepared powder was analysed by XRD synthesis to confirm that the product was U3O8. The SEM image showed the unique honeycomb structure.
کلیدواژه ها:
نویسندگان
Hadi Malekmohammad
Energy engineering and physics department, Amirkabir University of Technology, P.O. Box: 15875-4413, Tehran, Iran,
Taher Yousefi
NFCRS, Nuclear Science and Technology Research Institute,Tehran, Iran.
Ahmad GharibGarakani
Energy engineering and physics department, Amirkabir University of Technology, P.O. Box: 15875-4413, Tehran, Iran.
Seyed Javad Ahmadi
NFCRS, Nuclear Science and Technology Research Institute,Tehran, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :