Study OF Rheological and Mechanical Properties Of (PEO-PEG) Blends
سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 362
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
SCMEMI13_154
تاریخ نمایه سازی: 6 بهمن 1395
چکیده مقاله:
This study includes measurement of some rheological and mechanical properties of polyethylene oxide (PEO) , (polyethylene oxide + polyethylene glycol) (PEO + PEG ) polymers by using solvent Dimethylformamide (DMF) at room temperature such as density and shear viscosity. Other types of viscosities , viscosity average molecular weight and effective molecular radius were theoretically calculated. These samples were prepared in different concentrations (0.1,0.2,…,0.8 g/ml) % as solutions then the additive (PEG) as (0.25 g ) and ( 0.5 g) respectively , where the samples were prepared by liquids mixture . Results show that there are an increases in the density values , shear viscosity , relative viscosity and intrinsic viscosity , with increasing concentration of (PEO) before and after adding (PEG) polymer. However it was found that the reduced viscosity of (PEO) and its additive are inversely proportional with concentrations . For mechanical properties we notes from figures that the speed ultrasonic remain constant also note that the speed ultrasonic values increased after the addition of (PEG) , while others decreased
کلیدواژه ها:
نویسندگان
Raheem G. Kadhim
Ph.D.Department of Physics, College of Science ,University of Babylon, Iraq,
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :