IMPROVEMENT OF CORROSION RESISTANCE OF MAGNESA-CHROME REFRACTORES BY NANOSZED TITANA AND MAGNESLA SOLS VACUUMMPREGNATION
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 350
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_128
تاریخ نمایه سازی: 10 تیر 1396
چکیده مقاله:
In this research two kinds of nanosized titania and magnesia sols were prepared and were vacuum impregnated in magnesia-chrome bricks and the samples were heat treated at 1000 oC subsequently. The penetration and corrosion resistance to copper and convertor slag of impregnated and unimpregnated magnesia-chromite brick samples were tested using static finger tests at 1600 oC for 3 hours. SEM micrographs, elemental line scans and X-ray mappings results shows a different microstructure of the impregnated sample as compared to the un-impregnated one. The influence of vacuum impregnation on copper slag corrosion resistance of magnesia-chrome refractories has also been evaluated. The results show that both sols could improve the magnesia-chrome bricks corrosion resistance in impregnation.
کلیدواژه ها:
نویسندگان
YOUSEF SAFAEINAEINI
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, University Tehran, Iran
ALI TALIMIAN
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Narmak, Iran
FARHAID GOLESTANTI-FARD
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Narmak, Iran
HAMID REZA ZARGAR
Department of Metals and Materials Engineering, University of British Columbia Vancouver, Canada