PREPARATION OF ATO75 ALLOY NANOPOWDERS BY MECHANCAL ALLOYING AND ANNEALNG
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 295
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_217
تاریخ نمایه سازی: 10 تیر 1396
چکیده مقاله:
Al7075(Al-5.6Zn-2.5Mg-1.6Cu) was successfully synthesized via controlled atmosphere ball milled for 1-20h using elemental powders as a raw materials. The MA powders were annealed at 300°C for 2h under vaccum of 10°torr. Powder characterization were studied by optical microscopy, SEM, XRD and Microhardness at different milling time. Particle size measurements and XRD analysis after 20h of milling showed the formation of 8 average particles size with mean grain size of 38mm. It was found that due to formation of solid solution and diffusion of Mg in Al matrix, lattice parameter of Al was increased after annealing.
کلیدواژه ها:
نویسندگان
R. BADRI
Department of Materials Engineering, Malek-ashtarUniversity of Technology, shahinshahr, Isfahan, Iran,
G.H. BORHANI
Department of Materials Engineering, Malek-ashtarniversity of Technology, shahinshahr, Isfahan, Iran,
k fARMANESH
Department of Materials Engineering, Malek-ashtarUniversity of Technology, shahinshahr, Isfahan, Iran,
KM. DEHNAWI
DepartmentofMaterial Engineering, Malek-ashtarniversity of Technology, shahinshahr, Isfahan, Iran