WEAR BEHAVIOUR OF B-AlMg, INTERMETALLICNANO PARTICLE REINFORCEDALUMINUMMATRXINANOCOMPOSITES
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 552
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_230
تاریخ نمایه سازی: 10 تیر 1396
چکیده مقاله:
Aluminium based metal matrix composites reinforced with B-AlMg2 intermetallic nanoparticle were prepared by mechanical milling and hot pressing methods. nanoparticles was synthesized by mechanical milling of pre-alloyed B-AlMg intermetallic compound ingot in attritor ball mill. The content of reinforcement in the composite was varied from 0 to 20% wt.%, to study the effect of particles concentration on wear. The composites were prepared by mechanical milling and hot pressing. Results clearly indicate that increasing the volume percentage of 3-AlMg2 nanoparticles in the composite improves both the hardness and the wear resistance. As the B-AlMg2 amount increases from 3 to 20 wt.% wear rate decreases by 60%. Nanocomposite revealed a low frictioncoefficient of 0.4 which are significantly lower than those obtained for pure Al matrix. SEM tests revealed complex combination of wear mechanisms on the surface of the worn test specimens. A transition in wear mechanism from delimitation to abrasive wear observed in high amounts of reinforcement.
کلیدواژه ها:
نویسندگان
ASHIKAN ZOLRILASATEN
Advanced Materials and Nanotechnology Research Lab, Faculty of Mechanical Engineering, KN. Toosi University of Technology, Tehran, Iran
MASOUD EMAMY
Center of Excellence for High Performance Materials, School of Metallurgy and Materials, University of Tehran, Tehran, Iran
RASOUL AZARI KHOSROSHAHI
Faculty of Materials Engineering, Sahand University of Technology, Tabriz, Iran
ALI SHOKUHFAR
Advanced Materials and Nanotechnology Research Lab, Faculty of Mechanical Engineering, KN. Toosi University of Technology, Tehran, Iran