گواهی نمایه سازی مقاله Effect of cooling bath on LLDPE microporous membrane structure in thermally induced phase separation

عنوان مقاله: Effect of cooling bath on LLDPE microporous membrane structure in thermally induced phase separation
شناسه (COI) مقاله: ICHEC07_198
منتشر شده در هفتمین کنگره ملی مهندسی شیمی در سال ۱۳۹۰
مشخصات نویسندگان مقاله:

Elham Shokri - MS.c Student of Chemical Engineering, Sahand University of Technology, Tabriz, Iran Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran
Reza Yegani - Assistant Professor of chemical Engineering of Sahand University of Technology, Tabriz, Iran . Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran
zahra godarzi - Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran
leila noori - Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran

خلاصه مقاله:
Thermally induced phase separation (TIPS) is versatile method for making microporous membranes. The purpose of this work is to investigate the coolingbath temperature and type effects on the membrane structure prepared via TIPS method. The morphology of the resulting membrane shows a typical bicontinuous structure. When quenching into water at different temperatures, a larger pore size was obtained at higher temperature. Pore sizes are about 0.7 μm, 1.2 μm, and 2.2 μm for the water cooling bath with 273K, 303K and 333K. Porosity and tensile tests confirm these results. When the composition of the coagulation bath is similar with the diluents, the chemical potential difference of diluents would be declinedand the concentration of diluent in polymer lean phase would be kept constant in stagnant condition which leads the droplets to grow and the pore size of the systemwill be larger. However in water cooling bath, the concentration of diluent in polymer lean phase decreased rapidly and pore size growth is decelerated which result is lower porosity

کلمات کلیدی:
Microporous membrane, Thermally induced phase separation, Linear low density polyethylene, Cooling bath effect