گواهی نمایه سازی مقاله Hot and Cold Tensile Behavior of Al 6061 Produced By Equal Channel Angular Pressing and Subsequent Cold Rolling

عنوان مقاله: Hot and Cold Tensile Behavior of Al 6061 Produced By Equal Channel Angular Pressing and Subsequent Cold Rolling
شناسه (COI) مقاله: JR_IJMF-2-1_004
منتشر شده در مجله شکل دهی مواد در سال ۱۳۹۴
مشخصات نویسندگان مقاله:

A.A Khamei - Department of Mining and Metallurgical Engineering, Amirkabir University of Technology, Tehran, Iran
K Dehghani - Department of Mining and Metallurgical Engineering, Amirkabir University of Technology, Tehran, Iran
S Bakhshi - Metallic Materials Research Center (MMRC-MA), Malkashtar University, Tehran, Iran
K Kalayeh - Department of Mechanical Engineering, University of Maryland, Baltimore County, USA

خلاصه مقاله:
The full annealing AA6061 aluminum alloy was subjected to severe plastic deformationvia the combination of equal channel angular pressing (ECAP) and cold rolling (CR) in order torefine its microstructure and to improve its mechanical properties. According to the results of hotand cold tensile tests, the combination of ECAP and CR significantly affected the final strengthand ductility of studied AA6061. Four passes of ECAP followed by 90% reduction in rolling led toabout 5.4 and 3.15 times increase in the yield and ultimate tensile strengths, respectively. Inaddition, the hot ductility and strain rate sensitivity were increased by applying ECAP plus CR.The changes in mechanical properties were attributed to the enhanced dislocation density and tothe reduced grain size. The results show that a decrease in grains/subgrains size (0.37 μm) and anincrease in the fraction of high angle grain boundaries, exhibited significant effect on the hotductility of higher severe plastic deformed sample.

کلمات کلیدی:
Severe plastic deformation, Ultrafine-Grain (UFG), 6061 Al alloy, Rolling, Hot ductility