Mohammad Javad Maleki - Ceramics Department, Materials and Energy Research Center (MERC), Karaj, Iran
Hudsa Majidian - Ceramics Department, Materials and Energy Research Center (MERC), Karaj, Iran
Sara Banijamali - Ceramics Department, Materials and Energy Research Center (MERC), Karaj, Iran
Mohammad Zakeri - Ceramics Department, Materials and Energy Research Center (MERC), Karaj, Iran

The present work aims to prepare a dense cordierite-based glass-ceramic through slip casting and consequent heat treatment procedures. In this regard, sintering conditions were considered as the key variables to improve the properties of the glass-ceramic. For this purpose, glass frit powder was prepared through melting oxide powders (in the system of SiO۲-Al۲O۳-TiO۲-K۲O-CaO-MgO). The mixed powders were then heat treated at ۱۴۵۰ °C for ۱ hour and quenched in water. The glass frit powder was slip cast using the appropriate dispersant. Sintering was carried out by one-step, two-step, and three-step procedures. Specimens were characterized in terms of various analysis techniques including dilatometry, X-ray diffractometry, scanning electron microscopy, and mechanical strength measurement. Among the examined specimens, the sample sintered by a three-step approach was considered the optimized one which attained zero porosity. According to the obtained results, cordierite crystals were observable in this glass-ceramic matrix. A low coefficient of thermal expansion and a low dielectric constant were observed for the optimized glass-ceramic sample. The obtained results confirmed that the homogenous distributions of crystalline phases are responsible for the appropriate and desirable properties of the prepared glass-ceramic.

Cordierite, Glass-ceramic, Slip casting, Sintering