Cathodic synthesis of Al-Ce-Mn Oxide nanohybride powder with improved surface for effective removal of fluoride from aqueous media

Al-Ce-Mn oxide samples were synthesized by the cathodic electrochemical method at current densities of ۵, ۱۵, and ۳۵ mAcm-۲. The XRD, SEM, and EDX techniques were used for the characterization of samples. The SEM images show that at high current density the one-dimensional(nanowire) structure and at low current density two-dimensional (nanosheet) structure were obtained. Moreover, the particle sizes are decreased with increasing the current density. The samples were applied for the uptake of fluorine (F-) ions from solutions. The influence of the contact time, initial fluoride concentration, and solution pH on the adsorption was investigated. The results showed more than ۸۰ % of F-  ions were uptake from solution during the three hours initial contact times and the uptake capacity has little change at pH below ۶ and it has a sharp decline with increasing solution pH. The kinetic data were well fitted to the pseudo-second-order model and the equilibrium adsorption data was well described by the Langmuir isotherm model.  The adsorption capacity was ۴۸ mg/g at pH ۶ and room temperature. 

کلیدواژه ها:

Al-Mn-Ce Oxide ، Adsorption ، fluoride ، Nanowire ، Electrodeposition