Modeling and Experimental Study of Pyroplastic Deformation for Ceramic Materials during Liquid Phase Sintering Process
محل انتشار: مجله سرامیک های پیشرفته، دوره: 3، شماره: 2
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 204
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ACERPT-3-2_003
تاریخ نمایه سازی: 11 اردیبهشت 1400
چکیده مقاله:
The effective shear and bulk viscosity, as well as dynamic viscosity, describe the rheological properties of the ceramic body during the liquid phase sintering process. The rheological parameters depend on the physical and thermo-mechanical characteristics of the material such as relative density, temperature, grain size, diffusion coefficient, and activation energy. Thermal behavior of the ceramic body during sintering process including the viscose flow deformation, anisotropic shrinkage, heterogeneous densification, as well as sintering stress, have significant influence on the both final body dimensional precision and densification process. In this paper, the numerical-experimental method has been developed to study both rheological and thermal behavior of hard porcelain ceramic body during liquid phase sintering process. After raw materials analysis, the standard hard porcelain mixture as a ceramic body was designed and prepared. The finite element method for the ceramic specimens during the liquid phase sintering process are implemented in the CREEP user subroutine code in ABAQUS. Densification results confirmed that the bulk viscosity was well-defined with relative density. It has been shown that the shrinkage along the normal axis of slip casting is about ۱.۵ times larger than that of casting direction. The stress analysis proved that the sintering stress is more than the hydrostatic stress during the entire sintering time so, the sintering process occurs completely. The inhomogeneity in Von-Misses, pressure, and principal stress intensifies the relative density non-uniformity. Dilatometry, SEM, XRD investigations as well as bulk viscosity simulation results confirmed that the “mullitisation plateau” was presented as a very little expansion at the final sintering stage, because of the highly amount of mullite formation.
کلیدواژه ها:
نویسندگان
Hamed Yaghoubi
Ceramic, Ceramic
Esmaeil Salahi
, Materials and Energy Research Center (MERC)
Fatemeh Taati-Asil
Dear Editorial Board: Enclosed is a manuscript to, Dear Editorial Board: Enclosed is a manuscript to
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :