Fabrication and Characterization of Nanostructure Functionally Graded Ni-P Electroless Coating
محل انتشار: فصلنامه مواد پیشرفته و فرآوری، دوره: 4، شماره: 1
سال انتشار: 1395
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 168
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-4-1_003
تاریخ نمایه سازی: 13 مهر 1400
چکیده مقاله:
In this research, novel functionally graded Ni-P coating was deposited with electroless process. The content of phosphorus was controlled to change gradual through the thickness of the coating. During the plating, bath temperature and pH were changed at specified intervals to obtain functionally graded structure. To compare the properties of functionally graded coating with Ni-P single-layer coatings, three types of coatings with different phosphorus contents were also deposited. Microstructure and phase composition of coatings were studied by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffractometry (XRD). The mechanical properties and tribological behavior of coatings were also investigated. Low phosphorus and medium phosphorus single-layer coatings had fully crystalline and amorphous-crystalline structures, respectively. While high phosphorus coating appeared to have a fully amorphous structure. TEM images showed that low phosphorus coating had nano-crystalline structure. Results of nano-indentation test showed gradual changes in hardness profile in cross-section of functionally graded coating due to the gradual changes of phosphorus content in the thickness of this coating. According to the wear test data, medium phosphorus coating had minimum wear resistance. Functionally graded coatings had better wear resistance than single-layer coatings.
کلیدواژه ها:
نویسندگان
Sayede Razieh Anvari
Young Researchers and Elite Club, Najafabad Branch, Islamic Azad University, Najafabad, Iran
Sayed Mahmoud Monirvaghefi
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
Mohammad Hossein Enayati
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :