Synthesis of a novel polymeric corrosion inhibitor and investigation of its improvement by the addition of a ceramic powder extracted from corn cob
محل انتشار: مجله بین المللی ابعاد نانو، دوره: 5، شماره: 3
سال انتشار: 1393
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 273
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJND-5-3_003
تاریخ نمایه سازی: 24 تیر 1401
چکیده مقاله:
A new anti-corrosion compound, Melamine Formaldehyde (MF), was formulated by the addition of proper amount of formaldehyde to melamine under specific conditions. This compound was mixed with a novel nano powder, which was extracted from corn cob ash containing SiO۲ particles, in order to improve its corrosion inhibition efficiency. This inhibitor provides a high level of protection for steel subjected to saline environments. The synthesized inhibitor works immediately with forming a dense protective layer and after adding the nano powder, its inhibition efficiency is improved. The electrochemical standard corrosion tests and the surface examination, using Scanning Electron Microscope (SEM) of steel specimen immersed in ۳.۵%Wt NaCl solutions with and without any inhibitor at room temperature, were carried out to investigate the inhibition behavior of the synthesized inhibitor. All of the results, which include the corrosion and electrochemical testing data, show that the tested corrosion inhibitor is generally effective and its efficiency gets better by adding the ceramic powder.
کلیدواژه ها:
Corrosion inhibitors ، Electrolyte ، Concentration ، Chemical nature ، Film forming corrosion inhibitor ، Corn cob ash
نویسندگان
Z. Sharifi
Department of Material Engineering, Shiraz University, Shiraz, Iran
M. Pakshir
Department of Material Engineering, Shiraz University, Shiraz, Iran
F. Ghofrani
Department of Material Engineering, Shiraz University, Shiraz, Iran
S. Babamohammadi
Department of Chemistry, Shiraz University, Shiraz, Iran.