Properties of Cement Pastes Doped with Very High Amounts of Ground Granulated Blast-furnace Slag
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 15، شماره: 2
سال انتشار: 1397
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 125
فایل این مقاله در 13 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-15-2_001
تاریخ نمایه سازی: 1 اسفند 1401
چکیده مقاله:
In the current work, the properties of cement pastes doped with high amounts of ground granulated blast-furnace slag (HVS) were investigated. Portland cement (PC) was substituted with ground granulated blast-furnace slag (donated as slag) at very high amounts of ۸۵%, ۹۰%, ۹۵% and ۱۰۰%, by weight. PC paste without any content of slag was used as a reference. Some fresh and hardened properties such as workability, density, compressive strength up to ۵۶ days, pH value and drying shrinkage up to ۲۰۰ days were measured. The various phases formed were identified using X-ray diffraction (XRD) and thermogravimetric analysis (TGA). The microstructure of the formed hydration products was determined by scanning electron microscopy (SEM). The results indicated that HVS has higher workability and higher drying shrinkage beyond ۶۰ days. On the other hand, HVS has lower pH, density and compressive strength.
کلیدواژه ها:
نویسندگان
A. Rashad
Building Materials Research and Quality Control Institute, Housing & Building National Research Center, HBRC, Cairo, Egypt
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :