Static Strain Aging Behavior of Low Carbon Steel Drawn Wire
محل انتشار: مجله شکل دهی مواد، دوره: 1، شماره: 0
سال انتشار: 1393
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 98
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMF-1-0_005
تاریخ نمایه سازی: 14 شهریور 1402
چکیده مقاله:
The static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. Thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. To do so, the wires are austenitized at different temperatures and cooled in different rates. Then the wires are drawn and aged at a specific temperature and time. Before and after aging of each drawn wire, the hardness distribution at its cross section is measured. The increase in hardness due to aging is called aging index. The results show that the hardness of drawn wire is increased from center to surface of its cross section. However, after aging the hardness is decreased from center to surface. In addition, with increasing the austenitizing temperature, the index is increased. Also, with increasing the cooling rate, the index is decreased. Moreover, the aging index is decreased from center to surface.
کلیدواژه ها:
نویسندگان
M. Kazeminezhad
Sharif University of Technology
Y. Khaledzadeh
sharif University of Technology
A. Karimi Taheri
Sharif University of Technology
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :