Effect of time and heat-treatment temperatures on the characterization of nano-crystallite Mn1.5Co1.5O4 prepared by citrate sol–gel method
محل انتشار: هفتمین کنگره ملی مهندسی شیمی
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 645
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_498
تاریخ نمایه سازی: 25 فروردین 1394
چکیده مقاله:
Mn1.5Co1.5O4 based spinels are of great interest as raw materials in coating of interconnects in solid oxide fuel cells. Nano-crystalline Mn1.5Co1.5O4 spinels have been synthesized from aqueous solution of metal nitrate containing citric acid as a chelating agent using sol-gel method. The effect of annealing time and temperature were also evaluated at various annealing times (2h, 4h) and annealing temperatures (800, 950, 1050 oC) through X-Ray Diffraction (XRD) analysis to optimize the amount of nano-crystalline Mn1.5Co1.5O4. Results showed that the calcination temperature and time are playing significant roles in the formation of the single-phase and at the same time on the size of nano-crystalline Mn1.5Co1.5O4. More Mn1.5Co1.5O4 was obtained at higher temperatures and longer times as lower temperatures and shorter times were resulted in Mn1.5Co1.5O4 with smaller crystallite size .The optimum time and temperature were selected to synthesize Mn1.5Co1.5O4 with smallest size. The thermal behavior of the material has been examined by Thermogravimetry (TG) and Differential Thermal Analysis (DTA).
کلیدواژه ها:
نویسندگان
S. Tahereh Hashemi
Material Science & Engineering Department, Sharif University of Technology, Tehran, Iran
Niloofar Soltani
Material Science & Engineering Department, Sharif University of Technology, Tehran, Iran
Amirmasoud Dayaghi
Material Science & Engineering Department, Sharif University of Technology, Tehran, Iran
Masoud Askari
Material Science & Engineering Department, Sharif University of Technology, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :