Evaluation of morphology and cell behaviour of a novel synthesized electrospun poly(vinyl pyrrolidone)/poly(vinyl alcohol)/hydroxyapatite nanofibers
محل انتشار: مجله علوم نانو، دوره: 4، شماره: 2
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 438
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_NAMJ-4-2_006
تاریخ نمایه سازی: 18 تیر 1398
چکیده مقاله:
Objective(s): Three-dimensional structures such as nanofibrous scaffolds are being used in biomedical engineering as well as provide a site for cells to attach and proliferate leading to tissue formation. In the present study, poly(vinyl pyrrolidone) (PVP)/ poly(vinyl alcohol)(PVA) hybrid nanofibrous scaffold was synthesized by electrospinning. Materials and Methods: The effect of adding nano hydroxyapatite (n-HA) and also Epoxypropoxy-propyl-trimethoxysilane (EPPTMS) as a crosslinking agent on morphology and cell behaviour of the nanofibers was investigated.Results: Scanning electron microscope (SEM) observations showed that all kinds of nanofibers represented uniform and well-ordered morphologies without formation of any beads by controlling the synthesis parameters. The average ûber diameter of PVP-PVA was 260 nm. n-HA was synthesized by wet chemical process. The synthesized n-HA was characterized by XRD for structural analysis. Transmission electron microscope (TEM) revealed that HA particles had nanosized dimensions (in the range of 40-100 nm). The presence of n-HA within electrospun PVP-PVA nanofibers was confirmed by XRD and Fourier transmission infrared spectroscopy (FTIR) analyses. The average ûber diameter was decreased to 136 nm when n-HA was added in the composition of PVP-PVA. FTIR analysis depicted that PVP-PVA nanofibers were linked to EPPTMS as a biocompatible material by the covalent bond. Although adding n-HA caused to decrease the diameter of PVP-PVA nanofibers, addition of EPPTMS within PVP/PVA/n-HA nanofibers induced increasing distribution of fiber diameter as it enhanced to 195nm. In addition, the proper proliferation of G292 osteoblastic cells without any cytotoxicity was observed for the nanofiber.Conclusion: Since these materials have been known as biomaterials, PVP/PVA/n-HA-EPPTMS nanofibers can be propounded as a good candidate for bone tissue engineering application.
کلیدواژه ها:
نویسندگان
Raheleh Faridi-Majidi
Nanotechnology and Advanced Materials Department, Materials and Energy Research Center, Karaj, Alborz, Iran
Nader Nezafati
Nanotechnology and Advanced Materials Department, Materials and Energy Research Center, Karaj, Alborz, Iran
Mohammad Pazouki
Nanotechnology and Advanced Materials Department, Materials and Energy Research Center, Karaj, Alborz, Iran
Saeed Hesaraki
Nanotechnology and Advanced Materials Department, Materials and Energy Research Center, Karaj, Alborz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :