Effects of Boron and Zirconium on the Microstructure and High-Temperature Strength of Cast Fe3Al-Based Alloys
محل انتشار: مجله مواد دوستدار محیط، دوره: 1، شماره: 1
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 310
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JEFM-1-1_001
تاریخ نمایه سازی: 25 تیر 1398
چکیده مقاله:
In this study, the effects of boron (B) and zirconium (Zr) on the microstructure and high-temperature strength of Fe3Al-based alloys were investigated. Alloying was performed in a vacuum induction melting furnace (VIM) and, consequently, the melt then was poured into a cast iron mold. Microstructural investigation was conducted using optical and electron microscopy, X-ray diffraction, and differential thermal analysis. Addition of B and Zr to the alloys resulted in the formation of boride precipitates and Laves phases. Dendritic microstructures were found in as-cast alloys because of segregation of alloying elements into the interdendritic regions. To evaluate the high-temperature mechanical properties of the alloys, hot pressure test was performed. The results showed that, Zr exhibited the most pronounced effect on the high-temperature strength because of the formation of Laves phases. Boride phases tend to coarsen when increasing the temperature to 650°C, and they have no effect on the high-temperature strength of the alloy. In the temperature range of 450°C–550°C, an anomaly in the temperature-dependence of the yield strength was observed.
کلیدواژه ها:
نویسندگان
M. Rajabi
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran.
M. Shahmiri
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran.
M. Ghanbari
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :