Vacancy Defects Induced Magnetism in Armchair Graphdiyne Nanoribbon
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 54
فایل این مقاله در 24 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JOPN-4-4_002
تاریخ نمایه سازی: 25 بهمن 1402
چکیده مقاله:
Spin-polarized electronic and transport properties of Armchair GraphdiyneNanoribbons (A-GDYNR) with single vacancy (SV), two types of configurations fordouble vacancy (DV۱, DV۲) and multi vacancy (MV) defects are studied by nonequilibriumGreen’s function (NEGF) combined with density functional theory (DFT).The results demonstrate that the A-GDYNR with the SV has the lowest formationenergy and the most energetically favorable. The SV induces a ۲.۰۸ μB magneticmoment while the DV۲ possess no magnetism into A-GDYNR. Analyzing the bandstructures shows that the perturbation in A-GDYNR caused by the SV, DV۱ and MVbreaks the degeneracy and appears new bands around the Fermi level which indicate astrong spin splitting. Moreover, using density of states (DOS) analysis, it is illustratedthat the appeared flat bands correspond to the localized states which mainly contributeby the carbon atoms near the vacancies. The calculated current-voltage characteristicsfor A-GDYNR with the SV, DV۱, and MV reveal that the spin degeneracy is obviouslybroken. As well, a high spin-filtering efficiency around ۹۰% is found at the bias voltageof ۰.۳V for A-GDYNR with the SV. Our findings illustrate that we can obtain AGDYNRswith especial magnetic properties by removing carbon atoms from AGDYNR.
کلیدواژه ها:
نویسندگان
Somayeh Fotoohi
Department of Electrical Engineering, Islamshahr Branch, Islamic Azad University, Islamshahr, Iran
Saeed Haji Nasiri
Faculty of Electrical, Biomedical and Mechatronics Engineering, Qazvin BranchIslamic Azad UniversityQazvinIran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :