An Investigation on the Cracks and Hot Corrosion-like Failures in AISI 310 Flare Tips of South Pars Gas Complex
محل انتشار: دهمین همایش مشترک و پنجمین کنفرانس بین المللی انجمن مهندسی مواد و متالورژی و انجمن علمی ریخته گری ایران
سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 462
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES10_168
تاریخ نمایه سازی: 6 اردیبهشت 1396
چکیده مقاله:
The flare system in gas refineries collects hydrocarbon gases released from relief valves during upset conditions, process venting during start-up and blow down gas during normal shutdown and emergency conditions. So, having an intact flaring system is one of the most fundamental requirements in gas refineries in order to have gas production continuity, Specially in emergency flaring during unexpected shut downs. Since stainless steel grade AISI 310 has a good resistance against high temperature oxidation and hot corrosion, it has been used extensively in the construction of most flare tips in refineries. In this paper we have been focused on failure analysis of cracks and corrosion-like failure which occurred on medium pressure flare tips after short period of being in service. In order to investigate root causes of the failure, some samples taken from cracked and corroded areas and metallographic analysis was done. Results of microscopic examinations containing SEM, EDS and micro hardness measurements revealed Intergranular corrosion due to the occurrence of chromium depletion around the grain boundaries. Diffraction pattern of XRD examination on the burned parts of the pilot indicated high levels of oxygen which can be the result of high temperature oxidation. Low distance between high and medium pressure flares and consequent flame impingement due to predominant wind direction and retention rings improper design concluded as root causes in this kind of failure.
نویسندگان
Askar Soltani
Senior Corrosion Inspector , Phase 12 Gas Refinery, South pars Gas Complex
Koorosh Farzanfar
Head of Mechanical Inspection Department,
Reza Zarei
Head of Inspection Department,
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :