Investigation on microhardness distribution of HPT-consolidated pure aluminum powder disks and study on the reason of their high thermal stability
محل انتشار: دهمین همایش مشترک و پنجمین کنفرانس بین المللی انجمن مهندسی مواد و متالورژی و انجمن علمی ریخته گری ایران
سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 513
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES10_389
تاریخ نمایه سازی: 6 اردیبهشت 1396
چکیده مقاله:
The high pressure torsion (HPT) is a good and effective method for consolidation of different powders by combination of high imposed pressure during torsional straining. In the presentinvestigation, commercial pure aluminum powder were consolidated to dense disks by means of HPT process under 600 kN applied force and 1, 2 and 4 number of turns. For comparison, a few samples were also produced by simple uniaxial pressing -HPT-consolidated samples were annealed under argon atmosphere at 350,450 and 550 C for 1 hour. The microhardness test wascarried out on the cross section of disks on the distance of 0.3 mm along the diameter and thickness for as-fabricated and annealed disks. The data of microhardness were plotted in colorcodedcontour maps of microhardness for each sample. The results showed that by increasing number of turns and distance from the center of disks, the value of microhardness increases. The microhardness distribution for simple compacted disks was uniform the trend of microhardness distribution was unchanged up to 450 for sample processed with 4 number of turns that implies to the high thermal stability of HPT-consolidated disks. By increasing annealing temperature up to 550 C, the microhardness values decreases and the maps transformed to uniform distribution
کلیدواژه ها:
Severe plastic deformation (SPD) ، high pressure torsion (HPT) ، color-coded contour maps ، microhardness distribution ، high thermal stability ، powder metallurgy
نویسندگان
Mohammad Khajouei Nezhad
Graduate Student, Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran
Mohammad Hossein Paydar
Proffesor, Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran