Synthesis and characterization of 13X zeolite powder
سال انتشار: 1389
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 3,136
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
TOIL01_162
تاریخ نمایه سازی: 4 اسفند 1389
چکیده مقاله:
Zeolite 13X powders are of the major categories of zeolites and have a great potential to be employed industrially in many applications including gas separation tasks, e.g. CO2 and H S removal form natural gas by separation by adsorption, especially for CO2Effects of SiO2 /Al2 O3,H2 O/Na2O3and H2 O/SiO2 molar ratios was investigated on13X zeolite hydrothermal synthesis. Prepared powders was characterized using XRD analysis It was found that silica source, synthesis temperatures, and H O/Na O molar ratios are affecting parameters in zeolite13X synthesis and its crystalinity The best result was found for 1 Al2 O3;2.9 SiO2:4.35Na2O;304.5H2O at synthesis temperature of 110°C in5 h with aging time of 24 h.
کلیدواژه ها:
نویسندگان
Toraj Mohammadi
Islamic Azad University, South Tehran Branch, Department of Chemical Engineering
Majid Badini Pour Azar
Tehran Refinary (Shahid Tond Gooyan), National Oil Product and Distillation Co., Tehran
Mansoor Kazemi Moghadam
Islamic Azad University, South Tehran Branch, Department of Chemical Engineering
Omid Bakhtiari
Research Center for Membrane Separation Processes Department of Chemical Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran,
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :