Mechanical Properties of Low Plasticity Clay Soil Stabilized with Iron Ore Mine Tailing and Portland Cement
محل انتشار: مجله معدن و محیط زیست، دوره: 11، شماره: 3
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 287
فایل این مقاله در 17 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMAE-11-3_014
تاریخ نمایه سازی: 21 اردیبهشت 1400
چکیده مقاله:
Due to economical and environmental issues, utilization of mineral wastes, e.g. iron ore mine tailing (IOMT), as road materials can be recommended as a sustainable alternative. In the present study, mechanical properties, as well as resistance to freezing and thawing cycles (F-T) of low plasticity clay soil stabilized with different percentages of Portland cement (۰, ۶, ۹, ۱۲ and ۱۵%) and different IOMT content (۰, ۱۰, ۲۰, ۳۰ and ۴۰%) has been investigated. To this end, unconfined compressive strength (UCS), initial elastic modulus (E۰), and indirect tensile strength (ITS) at different curing times of ۷, ۱۴, ۱۸, and ۵۶ days for different admixtures was determined to select optimum mix design for stabilization of clayey subgrade soil. This study shows that by increasing the percentage of cement, strength parameters such as UCS, E۰, and ITS increases while increasing IOMT does not show a specific trend to increase strength parameters. Evaluation of strength parameters at different curing time showed that in short-term curing times (۷ and ۱۴ days), iron ore mine tailing has a positive effect on the strength parameters, while in long-term curing times (۲۸ and ۵۶ days), iron ore mine tailing has a negative effect on the strength parameters. In total, it was found that ۱۲% of the Portland cement and ۱۰ to ۴۰% of the IOMT passes the UCS and F-T criteria for stabilization of low plasticity clay soils, while clay soil (without IOMT) requires at least ۱۵% of Portland cement for stabilization.
کلیدواژه ها:
نویسندگان
A. R. Ghanizadeh
Department of Civil Engineering, Sirjan University of Technology, Sirjan, Iran
A. Yarmahmoudi
Department of Civil Engineering, Sirjan University of Technology, Sirjan, Iran
H. Abbaslou
Department of Civil Engineering, Sirjan University of Technology, Sirjan, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :