Investigation of Fracture Toughness of Shotcrete using Semi-Circular Bend Test and Notched Brazilian Disc test; Experimental Test and Numerical Approach
محل انتشار: مجله معدن و محیط زیست، دوره: 14، شماره: 1
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 138
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMAE-14-1_014
تاریخ نمایه سازی: 28 فروردین 1402
چکیده مقاله:
This work presents the Semi-Circular Bend (SCB) test and Notched Brazilian Disc (NBD) test of shotcrete using experimental test and Particle Flow Code in two-dimensions (PFC۲D) in order to determine a relation between mode I fracture toughness and the tensile strength of shotcrete. Firstly, the micro-parameters of flat joint model are calibrated using the results of shotcrete experimental test (uniaxial compressive strength and splitting tensile test). Secondly, numerical models with edge notch (SCB model) and internal notch (NBD model) with diameter of ۱۵۰ mm are prepared. Notch lengths are ۲۰ mm, ۳۰ mm, and ۴۰ mm. The tests are performed by the loading rate of ۰.۰۱۶ mm/s. Tensile strength of shotcrete is ۳.۲۵ MPa. The results obtained show that by using the flat joint model, it is possible to determine the crack growth path and crack initiation stress similar to the experimental one. Mode I fracture toughness is constant by increasing the notch length. Mode I fracture toughness and tensile strength of shotcrete can be related to each other by the equation, σt = ۶.۷۸ KIC. The SCB test yields the lowest fracture toughness due to pure tensile stress distribution on failure surface.
کلیدواژه ها:
نویسندگان
Mohammad Omidi manesh
Mining Engineering Department, Hamedan University of Technology, Hamedan, Iran
Vahab Sarfarazi
Mining Engineering Department, Hamedan University of Technology, Hamedan, Iran
Nima Babanouri
Mining Engineering Department, Hamedan University of Technology, Hamedan, Iran
Amir Rezaei
Mining Engineering Department, Hamedan University of Technology, Hamedan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :