Effect of combined different sources of alumina silicate on mechanical properties and carbonation depth of environmentally friendly geopolymeric composite based on metakaolin
محل انتشار: ماهنامه بین المللی مهندسی، دوره: 36، شماره: 7
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 82
نسخه کامل این مقاله ارائه نشده است و در دسترس نمی باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-36-7_017
تاریخ نمایه سازی: 7 خرداد 1402
چکیده مقاله:
Today, concrete is the most widely used building material. Cement production releases about ۷% of carbon dioxide gas into the atmosphere and increases greenhouse gases, so it seems necessary to use an alternative to Portland cement. In recent years, geopolymers (mineral polymers) have been proposed as a new environmentally friendly cement. Metakaolin, bentonite, zeolite, iron blast furnace slag and fly ash can be mentioned as aluminosilicate sources. In the field of geopolymer concrete construction, few articles have been working on the composition and effect of replacing aluminosilicate sources. In this laboratory study, the effect of replacing slag aluminosilicate sources, class F fly ash and bentonite with proportions of ۵-۴۵% with metakaolin on the mechanical properties and durability of geopolymer concrete based on metakaolin was investigated. After making the samples, compressive, bending, tensile and carbonation tests were performed on the geopolymer concrete samples to obtain the optimal strength and carbonation depth of the samples. Also, to determine the validity of the tests, machine learning estimation analysis was performed on the samples. The findings showed that bentonite leads to a decrease in strength, while fly ash and slag lead to an increase in strength. The predicted R۲ values showed the highest matching of the correlation matrix (more than ۹۳%) for the pressure samples. In addition, the results of the tests showed that the metakaolin-based geopolymer concrete sample replaced with fly ash (۳۵%) has a lower penetration depth (carbonation) and higher mechanical properties than other samples.
کلیدواژه ها:
نویسندگان
Alireza Esparham
Department of Environmental Engineering, University of Tehran, Tehran, Iran
Naser Mehrdadi
Department of Environmental Engineering, University of Tehran, Tehran, Iran