Impact of ultrasound frequency on the corrosion resistance of electroless nickel-phosphorus-nanodiamond plating
محل انتشار: مقالات مروری و پژوهشی شیمی، دوره: 5، شماره: 3
سال انتشار: 1401
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 80
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_CHRL-5-3_004
تاریخ نمایه سازی: 15 مرداد 1402
چکیده مقاله:
The nickel-phosphorus (Ni-P) and nickel-phosphorus-nanodiamond (Ni-P-ND) coatings were deposited on mild steel via electroless plating without ultrasound and under ultrasonic agitation with different frequencies of ۲۵, ۵۰, ۷۵, ۱۰۰, and ۱۵۰ kHz. The as-prepared coatings were characterized using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and X-ray diffraction (XRD). The corrosion performance of the fabricated layers was evaluated in ۳.۵ wt% NaCl solution by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization. Results of the corrosion tests demonstrated that deposition under ultrasonic power provided coatings with higher stability in the corrosive environment. The corrosion rate decreased with increasing ultrasound frequency from ۲۵ to ۷۵ kHz but increased with further increase in frequency. This introduced ۷۵ kHz as the optimum ultrasound frequency for electroless plating of Ni-P. It was also observed that the corrosion resistance of the proposed coating was improved through the incorporation of ۴۰ ppm nanodiamond into the Ni-P matrix.
کلیدواژه ها:
نویسندگان
Habib Ashassi-Sorkhabi
Electrochemistry Research Laboratory, Department of Physical Chemistry, Faculty of Chemistry, University of Tabriz, Tabriz, Iran
Amir Kazempour
Electrochemistry Research Laboratory, Department of Physical Chemistry, Faculty of Chemistry, University of Tabriz, Tabriz, Iran
Jafar Mostafaei
Electrochemistry Research Laboratory, Department of Physical Chemistry, Faculty of Chemistry, University of Tabriz, Tabriz, Iran
Elnaz Asghari
Electrochemistry Research Laboratory, Department of Physical Chemistry, Faculty of Chemistry, University of Tabriz, Tabriz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :