Two efficient approaches for improving field emission properties of ZnO NRs
محل انتشار: فصلنامه ادوات مخابراتی، دوره: 6، شماره: 1
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 91
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_TDMA-6-1_002
تاریخ نمایه سازی: 16 مرداد 1402
چکیده مقاله:
The structure of pure and Al doped ZnO (AZO) nanorods (NRs) has been studied. A post annealing procedure in oxygen ambience at ۴۰۰ﹾC were used in order to improve crystallinity of both group of samples. The XRD patterns illustrate that the Al doped ZnO NRs were successfully synthesized using our method. Then, the field emission properties of the as grown NRs before and after annealing process were evaluated by our home-made setup. Experimental results show that Al density in ZnO NRs directly affects FE properties of these samples. The oxygen post annealing process leads to a significant improvement in the field emission performances of pristine and doped ZnO NRs including considerably lower turn on voltage, and higher emission current.
کلیدواژه ها:
نویسندگان
Marziyeh Advand
Babol Noshirvani University of Technology
Bahram Azizollah Ganji
Babol Noshirvani University of Technology
Mohammad Reza Kolahdouz
University of Tehran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :