Properties of Fly Ash-Slag-Based Geopolymer Concrete with Low Molarity Sodium Hydroxide
محل انتشار: ژورنال مهندسی عمران، دوره: 9، شماره: 2
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 26
فایل این مقاله در 12 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_CEJ-9-2_010
تاریخ نمایه سازی: 2 اردیبهشت 1403
چکیده مقاله:
Most geopolymer concrete is produced using low-calcium fly ash and cured at high drying temperatures. Additionally, the activator is prepared with a sodium hydroxide (SH) solution of high molarity. This research proposes using a low molarity SH solution to produce fly ash-slag-based geopolymer concrete cured at room temperature. The properties to be investigated include workability, water absorption, and compressive strength. The influence of mixture composition, i.e., slag content, sodium silicate to sodium hydroxide (SS/SH) ratio, and alkaline activator to binder (Al/Bi) ratio on those properties is of interest. The slag substituted fly ash at ۱۰, ۲۰, ۳۰, ۴۰, and ۵۰% replacement levels. The SS/SH ratio is ۱.۰, ۱.۵, and ۲.۰, with the SH molarity determined at ۲M. The Al/Bi ratio is ۰.۴۰, ۰.۴۵, and ۰.۵۰. The results show that a higher percentage of slag reduces slump and water absorption but increases the compressive strength of the geopolymer concrete. The mixtures suitable for use are at the percentages of slag ۲۰, ۳۰, and ۴۰%. An increase in the SS/SH ratio decreases the slump and water absorption. Geopolymer concrete with an SS/SH ratio of ۱.۵ gives maximum compressive strength compared to the other ratios. Increasing the ratio of Al/Bi increases the workability of geopolymer concrete. At an Al/Bi ratio of ۰.۴۵, the compressive strength is maximum and the water absorption is minimum. The recommended mix design in terms of workability, water absorption, and compressive strength of geopolymer concrete is a mixture with slag contents of ۲۰, ۳۰, and ۴۰%, a SS/SH ratio of ۱.۰ and ۱.۵, and an Al/Bi ratio of ۰.۴۵ and ۰.۵۰. Doi: ۱۰.۲۸۹۹۱/CEJ-۲۰۲۳-۰۹-۰۲-۰۱۰ Full Text: PDF
کلیدواژه ها:
Low Molarity Sodium Hydroxide ، Workability ، Water Absorption ، Compressive Strength ، Slag ، Geopolymer Concrete.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :